Water-based metal cleaning agent
Technical Field The present invention relates to water-based cleaning agent for metals. Background Art My metal cleaning the metal cleaning agent widely used, mainly all kinds of solvents, the alkaline or acidic water-based cleaning agent solvent-based cleaning agent. Content of the invention The purpose of this invention is to provide a water-based metal cleaning agent, at room temperature to continue the oil speed is very rapid, low-temperature washing effect is extremely good, solvent-based and water-based cleaning agent has the double advantage of. To achieve the above object, the technical scheme of the invention is to design a water-based cleaning agent for metals, according to the weight portion is composed of the following composition: 75 parts of deionized water, 1-2 share hydroxy propyl methyl cellulose, 6-7 parts isopropanol, 5-6 sodium share molybdenum , 2-3 parts triazine multi-carboxylic acid compounds, 3-4 parts of diethylene glycol monobutyl ether, 2-3 parts of sodium benzoate, 1-2 copies of antifoamer, 2-3 parts lauryl alcohol, 1-2 parts sodium gluconate, 6-8 parts stearic acid polyethyleneoxide ester , 8-9 copies of malic acid, 3-4 parts laurel two acid, 5-6 parts fatty alcohol polyoxyethylene ether, 6-7 [...] , 2-3 parts isomerous tridecyl alcohol polyoxyethylene ether, 1-2 parts preservative, 8-9 three-ethanolamine, 2-3 parts plant oleic acid, 2-3 share boron ester. Preferably, water-based cleaning agent for metals, according to the weight portion is composed of the following composition: 75 parts of deionized water, 1.2 share hydroxy propyl methyl cellulose, 6.7 parts of isopropanol, 5.6 sodium share molybdenum , 2.3 parts triazine multi-carboxylic acid compounds, 3.4 parts of diethylene glycol monobutyl ether, 2.3 parts of sodium benzoate, 1.2 parts defoaming agent, 2.3 parts lauryl alcohol, 1.2 parts of sodium gluconate, 6.8 parts stearic acid polyethyleneoxide ester , 8.9 copies of malic acid, 3.4 parts laurel two acid, 5.6 parts fatty alcohol polyoxyethylene ether, 6.7 [...] , 2.3 parts isomerous tridecyl alcohol polyoxyethylene ether, 1.2 parts preservative, 8.9 three-ethanolamine, 2.3 parts plant oleic acid, 2.3 share boron ester. Preferably, water-based cleaning agent for metals, according to the weight portion is composed of the following composition: 75 parts of deionized water, 2 share hydroxy propyl methyl cellulose, 7 parts of isopropanol, 6 sodium share molybdenum , 3 parts triazine multi-carboxylic acid compounds, 4 parts of diethylene glycol monobutyl ether, 3 parts of sodium benzoate, 2 copies of antifoamer, 3 parts of sodium lauryl, 2 parts of sodium gluconate, 8 parts of stearic acid polyethyleneoxide ester , 9 copies of malic acid, 4 parts laurel two acid, 6 parts fatty alcohol polyoxyethylene ether, 7 [...] , 3 parts of heterogeneous tridecyl alcohol polyoxyethylene ether, 2 parts preservative, 9 parts of triethanolamine, 3 parts of plant oleic acid, 3 share boron ester. Preferably, water-based cleaning agent for metals, according to the weight portion is composed of the following composition: 75 parts of deionized water, 1 share hydroxy propyl methyl cellulose, 6 parts of isopropanol, 5 sodium share molybdenum , 2 parts triazine multi-carboxylic acid compounds, 3 parts of diethylene glycol monobutyl ether, 2 parts of sodium benzoate, 1 parts defoaming agent, 2 parts of sodium lauryl, 1 parts of sodium gluconate, 6 parts of stearic acid polyethyleneoxide ester , 8 copies of malic acid, 3 parts laurel two acid, 5 parts of polyoxyethylene fatty alcohol ether, 6 [...] , 2 parts of heterogeneous tridecyl alcohol polyoxyethylene ether, 1 parts preservative, 8 parts of triethanolamine, 2 parts of plant oleic acid, 2 share boron ester. The advantage of this invention and has the advantages of: providing a water-based metal cleaning agent, at room temperature to continue the oil speed is very rapid, low-temperature washing effect is extremely good, solvent-based and water-based cleaning agent has the double advantage of. Mode of execution The embodiment of combination, the specific implementation of the present invention further described manner. The following embodiment is used to more clearly illustrate the technical scheme of the invention, but not to limit the scope of protection of this invention. Implementation of the invention the technical scheme is: Embodiment 1 Water-based cleaning agent for metals, according to the weight portion is composed of the following composition: 75 parts of deionized water, 1.2 share hydroxy propyl methyl cellulose, 6.7 parts of isopropanol, 5.6 sodium share molybdenum , 2.3 parts triazine multi-carboxylic acid compounds, 3.4 parts of diethylene glycol monobutyl ether, 2.3 parts of sodium benzoate, 1.2 parts defoaming agent, 2.3 parts lauryl alcohol, 1.2 parts of sodium gluconate, 6.8 parts stearic acid polyethyleneoxide ester , 8.9 copies of malic acid, 3.4 parts laurel two acid, 5.6 parts fatty alcohol polyoxyethylene ether, 6.7 parts intermetallic barium aluminum compound, 2.3 parts isomerous tridecyl alcohol polyoxyethylene ether, 1.2 parts preservative, 8.9 three-ethanolamine, 2.3 parts plant oleic acid, 2.3 parts borate. Embodiment 2 Water-based cleaning agent for metals, according to the weight portion is composed of the following composition: 75 parts of deionized water, 2 share hydroxy propyl methyl cellulose, 7 parts of isopropanol, 6 sodium share molybdenum , 3 parts triazine multi-carboxylic acid compounds, 4 parts of diethylene glycol monobutyl ether, 3 parts of sodium benzoate, 2 copies of antifoamer, 3 parts of sodium lauryl, 2 parts of sodium gluconate, 8 parts of stearic acid polyethyleneoxide ester , 9 copies of malic acid, 4 parts laurel two acid, 6 parts fatty alcohol polyoxyethylene ether, 7 parts intermetallic barium aluminum compound, 3 parts of heterogeneous tridecyl alcohol polyoxyethylene ether, 2 parts preservative, 9 parts of triethanolamine, 3 parts of plant oleic acid, 3 parts borate. Embodiment 3 Water-based cleaning agent for metals, according to the weight portion is composed of the following composition: 75 parts of deionized water, 1 share hydroxy propyl methyl cellulose, 6 parts of isopropanol, 5 sodium share molybdenum , 2 parts triazine multi-carboxylic acid compounds, 3 parts of diethylene glycol monobutyl ether, 2 parts of sodium benzoate, 1 parts defoaming agent, 2 parts of sodium lauryl, 1 parts of sodium gluconate, 6 parts of stearic acid polyethyleneoxide ester , 8 copies of malic acid, 3 parts laurel two acid, 5 parts of polyoxyethylene fatty alcohol ether, 6 parts intermetallic barium aluminum compound, 2 parts of heterogeneous tridecyl alcohol polyoxyethylene ether, 1 parts preservative, 8 parts of triethanolamine, 2 parts of plant oleic acid, 2 copies of the borate. The stated above is the preferred embodiment of the invention, it should be noted that, in the technical field as the ordinary technical personnel, without departing from the present invention on the premise of the technical principle, can also be made a number of improvements and retouches, these improvements and retouches should also be regarded as the scope of protection of this invention. The invention discloses a water-based metal cleaning agent. The water-based metal cleaning agent comprises the following components in parts by weight: 75 parts of de-ionized water, 1-2 parts of hydroxypropyl methyl cellulose, 6-7 parts of isopropanol, 5-6 parts of sodium molybdate, 2-3 parts of triazine polycarboxylic acid compounds, 3-4 parts of diethylene glycol butyl ether, 2-3 parts of sodium benzoate, 1-2 parts of antifoaming agent, 2-3 parts of laurinol, 1-2 parts of sodium gluconate, 6-8 parts of polyoxyethylene stearates, 8-9 parts of polymalic acid, 3-4 parts of dodecanedioic acid, 5-6 parts of fatty alcohol-polyoxyethylene ether, 6-7 parts of benzotriazole, 2-3 parts of iso-tridecanol polyoxyethylene ether, 1-2 parts of preservative, 8-9 parts of triethanolamine, 2-3 parts of vegetable oleic acid, and 2-3 parts of borate. The water-based metal cleaning agent has quicker oil stain removing speed and better low-temperature cleaning effect under normal temperature. 1. Water-based cleaning agent for metals, characterized in that according to the weight portion is composed of the following composition: 75 parts of deionized water, 1-2 share hydroxy propyl methyl cellulose, 6-7 parts isopropanol, 5-6 sodium share molybdenum , 2-3 parts triazine multi-carboxylic acid compounds, 3-4 parts of diethylene glycol monobutyl ether, 2-3 parts of sodium benzoate, 1-2 copies of antifoamer, 2-3 parts lauryl alcohol, 1-2 parts sodium gluconate, 6-8 parts stearic acid polyethyleneoxide ester , 8-9 copies of malic acid, 3-4 parts laurel two acid, 5-6 parts fatty alcohol polyoxyethylene ether, 6-7 parts intermetallic barium aluminum compound, 2-3 parts isomerous tridecyl alcohol polyoxyethylene ether, 1-2 parts preservative, 8-9 three-ethanolamine, 2-3 parts plant oleic acid, 2-3 parts borate. 2. Water-based cleaning agent for metals according to Claim 1, characterized in that according to the weight portion is composed of the following composition: 75 parts of deionized water, 1.2 share hydroxy propyl methyl cellulose, 6.7 parts of isopropanol, 5.6 sodium share molybdenum , 2.3 parts triazine multi-carboxylic acid compounds, 3.4 parts of diethylene glycol monobutyl ether, 2.3 parts of sodium benzoate, 1.2 parts defoaming agent, 2.3 parts lauryl alcohol, 1.2 parts of sodium gluconate, 6.8 parts stearic acid polyethyleneoxide ester , 8.9 copies of malic acid, 3.4 parts laurel two acid, 5.6 parts fatty alcohol polyoxyethylene ether, 6.7 parts intermetallic barium aluminum compound, 2.3 parts isomerous tridecyl alcohol polyoxyethylene ether, 1.2 parts preservative, 8.9 three-ethanolamine, 2.3 parts plant oleic acid, 2.3 parts borate. 3. Water-based cleaning agent for metals according to Claim 1, characterized in that according to the weight portion is composed of the following composition: 75 parts of deionized water, 2 share hydroxy propyl methyl cellulose, 7 parts of isopropanol, 6 sodium share molybdenum , 3 parts triazine multi-carboxylic acid compounds, 4 parts of diethylene glycol monobutyl ether, 3 parts of sodium benzoate, 2 copies of antifoamer, 3 parts of sodium lauryl, 2 parts of sodium gluconate, 8 parts of stearic acid polyethyleneoxide ester , 9 copies of malic acid, 4 parts laurel two acid, 6 parts fatty alcohol polyoxyethylene ether, 7 parts intermetallic barium aluminum compound, 3 parts of heterogeneous tridecyl alcohol polyoxyethylene ether, 2 parts preservative, 9 parts of triethanolamine, 3 parts of plant oleic acid, 3 parts borate. 4. Water-based cleaning agent for metals according to Claim 1, characterized in that according to the weight portion is composed of the following composition: 75 parts of deionized water, 1 share hydroxy propyl methyl cellulose, 6 parts of isopropanol, 5 sodium share molybdenum , 2 parts triazine multi-carboxylic acid compounds, 3 parts of diethylene glycol monobutyl ether, 2 parts of sodium benzoate, 1 parts defoaming agent, 2 parts of sodium lauryl, 1 parts of sodium gluconate, 6 parts of stearic acid polyethyleneoxide ester , 8 copies of malic acid, 3 parts laurel two acid, 5 parts of polyoxyethylene fatty alcohol ether, 6 [...] , 2 parts of heterogeneous tridecyl alcohol polyoxyethylene ether, 1 parts preservative, 8 parts of triethanolamine, 2 parts of plant oleic acid, 2 share boron ester.