ARTIFICIAL MARBLE COMPOSITION, ARTIFICIAL MARBLE USING SAME AND METHOD FOR MANUFACTURING ARTIFICIAL MARBLE
Artificial marble composition, the artificial marble and scagliola manufacturing method using the same are disclosed. Recent marble has marble alternate use as to penetrate through and soft texture material as ficus, excellent workability, weather resistance and have excellent endurance and the like can be used in various. Artificial marble due to such properties e.g., sink, basin, bath, bank and general shop of receipt unit upper counter space, sill, furniture, hospital, such as a building plate inner wall, finishing material, can be used in various interior plastic. But, this artificial marble a pattern for representing an impression of marble cladding it is measured is lacking, artificial atmosphere or flow tides number to form a door. The, artificial marble pattern formed supercritical method and apparatus for implementing a usual approximate or marble are various method etc. inside. Such as filters of the present invention certain embodiments include marble beauty to the artificial marble pattern is implemented at the elongated amorphous number [...] substrate. One embodiment of the present invention, base resin composition; and colored resin composition; and, said base resin composition number 1 acrylic resin, number number 1 and number 1 acryl-based monomer and an inorganic filler, said colored resin composition number 2 acrylic resin, acryl-based monomer number 2, number 2 and number and draft free [...] inorganic filler, said number 2 acrylic resin weight-average molecular weight (Mw) weight-average molecular weight (Mw) is said number 1 acrylic resin composition number higher artificial marble [...] substrate. Another embodiment of the present invention, the composition for an artificial marble number said artificial marble [...] substrate. Another embodiment of the present invention, number 1 acrylic resin, an inorganic filler and a resin composition including the step number number number 1 number 1 acryl-based monomer and base tank; Number 2 acrylic resin, acryl-based monomer number 2, number 2 and number draft free colored resin composition including an inorganic filler [...] step number tank; said base resin composition and said colored resin composition by mixing artificial marble composition step number bath; the beauty of wood on said artificial marble composition of a sample (agitator) step; and said beauty are coated directly on the artificial marble composition for thermosetting step; and, said number 2 acrylic resin weight-average molecular weight (Mw) is higher than a weight-average molecular weight (Mw) said number 1 acrylic resin manufacturing method artificial marble number [...] substrate. Said cured product of the composition for an artificial marble extends long in the marble has amorphous collective line light from filters obtained by beauty to the beauty of wood on near marble patterns than can be. Figure 1 artificial marble surface photo as, in number in the embodiment 1 (is) is prepared by the artificial marble, (or) in number in the embodiment 2 is prepared by the artificial marble, in comparison example number 1 (disclosed) is prepared by the artificial marble, in comparison example 2 and the part of the surface of the artificial marble prepared by the number (as) is disclosed. Hereinafter, with reference to a drawing of the present invention in the embodiment for the present invention in the preface is provided to the person with skill in the art for detailed embodiment is hereinafter to 2000. The present invention refers to several different taught herein can be embodied in the form of a in the embodiment is not limited to. The present invention is described that is independent portion is unambiguously account for off disagreement. One embodiment of the present invention, base resin composition; and colored resin composition; and, said base resin composition number 1 acrylic resin, number number 1 and number 1 acryl-based monomer and an inorganic filler, said colored resin composition number 2 acrylic resin, acryl-based monomer number 2, number 2 and number and draft free [...] inorganic filler, said number 2 acrylic resin weight-average molecular weight (Mw) weight-average molecular weight (Mw) is said number 1 acrylic resin composition number higher artificial marble [...] substrate. The marble has beauty to the artificial marble pattern than said artificial marble composition number bath can be implementing close to the marble. Said artificial marble beauty to the colored resin composition composition patterns comprise a base resin composition constituting the background regions beauty to the patterns. Said colored resin composition whose design on the draft free [...] including composition and insert having sinusoidal beauty, beauty of wood on said base resin composition said colored resin composition can be appropriately mixing. Said colored resin composition mixing said base resin composition in order to uniformly mixed and they don't completely uniform beauty to the patterns, said colored resin composition said elongated base resin in the composition can be coated directly on the amorphous collective line filters a jacket thereof can bear. Such a collective line pattern of amorphous natural marble is equal to total may be combined as beauty to the rubber packing. Said artificial marble composition, draft free [...] colored resin composition including said weight average molecular weight of said base resin composition number 1 number 2 acrylic resin is an acrylic resin by having a weight average molecular weight higher than, said base resin composition can be blended to form a significantly clearer than amorphous collective line pattern. The clearer amorphous collective line pattern are gradually lowered, said artificial marble composition marble marble has prepared by the number is equal to or higher have approximate or equivalent levels of beauty to the pattern. Insert having sinusoidal marble order patterns, typically, base resin composition comprising inorganic chip, said clock synchronization method in the form of inorganic chip is separated, in which case filters a collective line pattern on the surface extends long since amorphous, a beauty to the marble patterns are difficult to door number flow tides. In another method, different color mixing method of parts resin composition is separated, in which case by the homo of resin composition, easy mixing of the composition can be improved but, while keeping the color cross each other resin composition through an address bar, bicycle and power clear number exists in the flow tides. Said artificial marble composition homogeneous resin, i.e., acrylic resin base resin composition and colored resin composition including mixing, base resin composition and easy mixing of the colored resin composition containing a charge generating material, simultaneously said colored resin composition included in weight average molecular weight of said base resin composition number 2 acrylic resin contained by weight average molecular weight of higher than number 1 acrylic resin, such as marble while elongated, amorphous collective line patterns beauty to the combination light patterns can be obtained. A combination of said base resin composition clear amorphous collective line pattern to be implemented by the adhesive sheet are colored resin composition method without a special spray method is defined which is, e.g., such as [...] method, said colored resin composition including said artificial marble beauty to the rubber composition can be applied to the stirring motion. Specifically, number 1 number 2 acrylic resin is an acrylic resin having a weight average molecular weight higher than said draft free and whose [...], [...] while moving along can be rubber. More specifically, said number 2 acrylic resin [...] trapping (trapping) wherein said draft free, while moves along said [...], placing said draft free [...] continue trapping may be formed thereof can. The, said draft free [...] outside said number 2 acrylic resin in the composition of the liquids without address, movement of number 2 acrylic resin along, and clear continue long patterns can be formed. Specifically, artificial marble included within the composition of said base resin composition (Mw) weight average molecular weight of about 6 to about 10 if only number 1 acrylic resin which, by having a weight average molecular weight in the range of ultraviolet said said number 1 (Mw), when the syrup and the number 1 which reacts with the acryl-based monomer, rubber layer containing an ethylene marble has prepared by the number therefrom be implementing strength and gravity. Specifically, the base resin artificial marble influence basic properties said bellows, said range has an weight-average molecular weight (Mw), base resin composition has number 1 acryl-based monomer easily bond which, the, dyeing or printing can be easily formed. Using said syrup number prepared by the marble has about 8 kgf/mm2 Or more high flexibility strength and about 1. 7 May have an excellent degree of gravity, cutting and for thermally processing hereinafter, at the height of about 1m or more artificial marble can be properties bear down to even if it is possible to implement. In addition, the weight average molecular weight of said number 2 acrylic resin (Mw) weight average molecular weight of about 12 to about 40 if said number 1 acrylic resin be higher than only. Specifically, about 12 to about 16 be only if said number 2 acrylic resin a weight average molecular weight. Said number 2 acrylic resin has an average molecular weight by weight ranging by said, base resin composition in said number 2 acrylic resin while forming a pattern, said pattern representing [...] draft free beauty to the continue trapping can be disclosed. In other words, by said said number 2 acrylic resin has an average molecular weight by weight ranging, draft free [...] coming spaced from said number 2 acrylic resin, in the form of a rounded mass while, artificial marble address can be in the composition prevent. The, said artificial marble composition extends long in the insert having sinusoidal prepared by the number filters amorphous collective line light from beauty to the pattern obtained by forming patterns near marble than can be beauty. In addition, said number 2 acrylic resin as included within the composition for forming patterns colored resin, an acrylic resin contained in the base resin composition with number 1, even a small amount can be beauty to the impact are patterns. The, number 1 with an acrylic resin, said acrylic resin having a weight average molecular weight in the range of number 2 (Mw) number 2 acryl-based monomer properly so that, can be easily and syrup. Said artificial marble composition beauty to the patterns along the shape of said base resin composition and said impact are colored resin composition can be gastric content. E.g., said base resin composition to said colored resin composition is 7:3 weight ratio can be from about 9:1. Said base resin composition to said colored resin composition weight ratio of said mixed composition to form said artificial marble, beauty to an appropriate level that the ratio patterns against background regions by forming a marble can be implementing near artificial marble. Said artificial marble composition included in said base resin composition viscosity and said colored resin composition has a viscosity from about about 25 °C 100Ps 65Ps implementation being. Said base resin composition and said of said colored resin composition have modified, artificial marble compositions can be mixed easily. Said artificial marble composition thus formed can be good flow in artificial marble composition further pore number artificial marble, the artificial marble both can be improved. In addition, warpage or marble has prepared by the number said artificial marble composition may not be generating bubbles traces, artificial marble quality number can be high pressure liquid coolant. In addition, said base resin composition viscosity said colored resin composition viscosity about any difference in implementation being 20Ps hereinafter. In [...] manufacturing method, said colored resin composition having a difference of said base resin composition viscosity viscosity by about 20Ps hereinafter, said base resin composition and said colored resin composition can be uniformly mixed or glass fiber compositions. The, said artificial marble number from a composition prepared by the marble has artificial marble beauty to the output pattern can be uniform throughout. In addition, about 100 parts by weight of said base resin composition number 1 acrylic resin, about 70 to about 400 parts by weight of an inorganic filler number number 1 number 1 acryl-based monomer parts by weight of about 150 to about 275 can be. In addition, about 100 parts by weight of said colored resin composition number 2 acrylic resin, about 100 to about 1,800 parts by weight of acryl-based monomer number 2, number 2 number about 90 to about 1,100 draft free about 0 parts by weight of an inorganic filler material. 1 To about 8. 0 Parts by weight of a can. Said base resin composition and said colored resin composition such as by including said content, including artificial marble composition may have the aforementioned same viscosity. Said base resin composition and said colored resin composition, said number 1 acrylic resin and said number 2 acrylic resin, independently, (meta) methyl methacrylate, ethyl (meta) methacrylate, butyl (meth) methacrylate, 2 - ethylhexyl (meth) methacrylate, benzyl methacrylate (meta), glycidyl (meta) selected from the group consisting a dimethylaminoethyl methacrylate and combinations thereof can be a polymer or copolymer. Said number 1 acrylic resin and said number 2 acrylic resin be the same or different. In addition, said number 1 acryl-based monomer and said number 2 acrylic monomers are, independently, (meta) methyl methacrylate, ethyl (meta) methacrylate, butyl (meth) methacrylate, 2 - ethylhexyl (meth) methacrylate, benzyl methacrylate (meta), glycidyl (meta) dimethylaminoethyl methacrylate and combinations thereof can be selected from the group consisting one. Said number 1 acryl-based monomer and said number 2 acryl-based monomer may be the same or can be different disclosed. In addition, inorganic filler is an inorganic filler and said number 2 number said number 1 number, independently, aluminum hydroxide, magnesium hydroxide, calcium carbonate, silica, alumina and combinations thereof can be selected from the group consisting one. An inorganic filler and an inorganic filler is said number 1 number said number 2 number be the same or different. An inorganic filler is an inorganic filler and said number 2 number said number 1 number dispersible resins, artificial marble and anti-silane coupling such as for the mechanical strength and number, comprising phosphorous coupling number number can be added. Said number 1 and number 2 number about 25 to about 100 micro m number mean particle size of the inorganic filler inorganic filler micro m implementation being. Said number 1 and number 2 number number by having an average particle diameter of said inorganic filler is an inorganic filler, artificial marble precipitates do not separated in the composition, including the aforementioned viscosity same artificial marble composition may have. Said artificial marble composition inorganic chip, crosslinked number, polymerization disclosure number and combination thereof can be selected from the group consisting further comprises addition of number one. Specifically, said inorganic chip is monochromatic resin composition or different colors by mixing resin composition number can be high pressure liquid coolant. Said inorganic chip number but not one specifically of the type, for example, resin or natural number from a material can be prepared by the inorganic chip. Natural number when said inorganic chip is connected to the high pressure liquid coolant, usual sacrificial Can be employed, examples thereof presenting, stone, stone powder, quartz, charcoal, loess, magnet component, perfume, pulse, comprising one or more selected from the group consisting of powder mirror and method of calcium can be, and pass it on one number are not disclosed. Said inorganic chip is, specifically, base resin can be included within the composition, the, marble can be more similar amorphous beauty to the rubber. E.g., as aforementioned, said colored resin composition included in said number 2 acrylic resin trapped free movement can be of wood on draft [...] stirring in passing along beauty. the base resin composition contained in the inorganic chip can be detachably engaging said [lyo and draft free while amorphous beauty to the pattern. I.e., beauty of wood on a natural marble-like amorphous can be easy. An average particle diameter of said inorganic chip about 0. 3 Mm to about 6. 8 Mm and can, by said size in the range of, said method and apparatus for artificial marble composition can close more marble beauty to the formed pattern. Said crosslinked copolymerizable double bonds in a molecular number including acrylic resin and cross-linking as the polyfunctional acrylic monomer, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, ethylene glycol dimethacrylate, tetra ethylene glycol dimethacrylate, tree [...] propane tree methacrylate, 1, 6 - hexanediol dimethacrylate, poly butylene glycol dimethacrylate, such as neopentyl glycol dimethacrylate and combinations thereof can be selected from the group consisting one. An organic peroxide is benzoyl peroxide as polymerization said disclosure number, such as a peroxide vulcanizable diacyl peroxide, butyl hydroperoxide, such as hydroperoxide [khwu wheat high draw a peroxide, t - butyl peroxy maleic acid, t - butyl hydroperoxide, it ladles, the jade father-in-law [thil the [ley the [thu t - butyl hydrogel, acetyl peroxide, lauroyl peroxide, azo bis isobutyrate methacrylonitrile, azo bis dimethyl ballet methacrylonitrile, t - butyl peroxy Neo car roh a [thu, t - amyl peroxy 2 - ethyl hexanoate, and combinations thereof can be selected from the group consisting one. Another embodiment of the present invention, the composition for an artificial marble number said artificial marble [...] substrate. As cured article obtained from said marble has the aforementioned artificial marble, extends long in the filters obtained amorphous collective line light from near has more marble pattern design on the beauty to the beauty. Another embodiment of the present invention, number 1 acrylic resin, an inorganic filler and a resin composition including the step number 1 number 1 acryl-based monomer and base number tank number; number 2 acrylic resin, acryl-based monomer number 2, number 2 and number draft free colored resin composition including an inorganic filler [...] step number tank; said base resin composition and said colored resin composition by mixing artificial marble composition step number bath; the beauty of wood on said artificial marble composition of a sample (agitator) step; and said beauty are coated directly on the artificial marble composition for thermosetting step; and, said number 2 acrylic resin weight-average molecular weight (Mw) is higher than a weight-average molecular weight (Mw) said number 1 acrylic resin manufacturing method artificial marble number [...] substrate. Said artificial marble manufacturing method by the aforementioned artificial marble number can be high pressure liquid coolant. I.e., elongated line light from amorphous collective filters obtained by beauty to the beauty of wood on artificial marble can be marble than near high pressure liquid coolant having a pattern number. Said manufacturing method is first artificial marble, number 1 acrylic resin, an inorganic filler and a resin composition including the step number number number 1 number 1 acryl-based monomer and base tank, and number 2 acrylic resin, acryl-based monomer number 2, number 2 and number [...] colored resin composition including an inorganic filler draft free bath a number comprising the following steps. The, said colored resin composition included in said number 1 number 2 acrylic resin a weight average molecular weight higher than the weight average molecular weight of acrylic resin base resin included within the composition. Said base resin composition and said colored resin composition content included in the aforementioned constituent and efined. The base resin composition and said colored resin composition said prepared by the number may have the aforementioned viscosity. In addition, base resin composition further comprises inorganic chip can be said. As aforementioned, said inorganic chip is said base resin composition contained in the colored resin composition contained in the beauty of wood on which impinges on said draft free while [lyo and can be amorphous. I.e., elongated line light from amorphous collective filters obtained by beauty to the beauty of wood on near marble than can be rubber. In addition, colored resin composition by mixing said base resin composition and said artificial marble composition bath a number comprising the following steps. As aforementioned, said artificial marble composition beauty to the patterns along the shape of said base resin composition and said impact are colored resin composition can be gastric content. E.g., said base resin composition to said colored resin composition is 7:3 weight ratio can be from about 9:1. Said base resin composition to said colored resin composition weight ratio of said mixed composition to form said artificial marble, beauty to an appropriate level that the ratio patterns against background regions by forming a marble can be implementing near artificial marble. In addition, the beauty of wood on said artificial marble composition of a sample (agitator) comprising the following steps. Stirring said colored resin composition including artificial marble composition provided on beauty of wood on while moving, e.g., on the direction of motion and said stirring artificial marble composition coefficient, the, can be beauty to the rubber. Generally, to form amorphous marble pattern, artificial marble composition in cases where the movement of a sample on the, rather, door number declined slowly faded out flow tides. While, elongated along said artificial marble composition stirring movement, can be continuously clear amorphous pattern formation. Specifically, number 1 number 2 acrylic resin is an acrylic resin having a weight average molecular weight higher than said draft free and whose [...], [...] while moving along can be rubber. More specifically, said number 2 acrylic resin [...] trapping (trapping) wherein said draft free, while moves along said [...], placing said draft free [...] continue trapping may be formed thereof can. The, said draft free [...] outside said number 2 acrylic resin in the composition of the liquids without address, along movement of number 2 acrylic resin, amorphous collective line extends long in the filters obtained light from beauty to the pattern can be formed continuously. Said stirring the display screen can be publicly known in the art kind using, not limited particularly. Said method include a method in addition to the artificial marble number bath, while mold base resin composition, using nozzle during mold base resin composition layer is formed on the colored resin composition for forming patterns method above may be disclosed. In addition, base resin composition colored resin composition after mixing, a mold method may be disclosed. Said method are both, number 1 number 2 acrylic-based resin having a weight average molecular weight average molecular weight of acrylic resin compositions can be used to higher artificial marble, artificial marble number bath method for gaskets, extends long in the marble has prepared by the number therefrom filters amorphous collective line light from beauty to the pattern obtained by forming patterns near marble than can be beauty. Said artificial marble beauty to the artificial marble are coated directly on the manufacturing method comprising the following steps for thermosetting composition. About 80 °C to about 100 °C is about 30 minutes for thermosetting said thermosetting of oven, through the aforementioned artificial marble number can be high pressure liquid coolant. In the embodiment of the present invention hereinafter are etched in the specific number. But, for the present invention are described in the embodiment or example specifically for gas and only to explain, the number is not one immediately after being turned off the present invention are disclosed. In the embodiment 1 8 Methyl methacrylate 95 parts by weight of 100 parts by weight of a weight average molecular weight for each methacrylates, 190 parts by weight of aluminum hydroxide, inorganic chip 40 parts by weight, including about 80Ps number 3 parts by weight of crosslinked base resin composition viscosity number was high pressure liquid coolant. Weight average molecular weight of 100 parts by weight of methyl methacrylate 178 for each 12 parts by weight of methyl methacrylate, 210 parts by weight of aluminum hydroxide, 7 parts by weight of crosslinked number 3 parts by weight of and white colored resin composition including about 75Ps draft free material viscosity number was high pressure liquid coolant. Said base resin composition to 9:1 to 20 times the weight ratio of a sample by mixing colored resin composition is rotated so that the high pressure liquid coolant composition was blended artificial marble number. Said artificial marble is poured in mold composition after-gate mold. The, mold [...] zigzag direction about 5 times during molds on artificial marble composition further degree beauty to the pattern moving weight percent. 30 Minutes at 90 °C thermosetting composition in an artificial marble number mold said artificial marble was high pressure liquid coolant. In the embodiment 2 A weight average molecular weight for each poly methyl meta [khu relay [thu 20 including the colored resin composition number [...] point number and high pressure liquid coolant, the artificial marble number the same method in the embodiment 1 was high pressure liquid coolant. Comparison example 1 A weight average molecular weight for each poly methyl meta [khu relay [thu 8 colored resin composition including the number [...] point number and high pressure liquid coolant, the artificial marble number the same method in the embodiment 1 was high pressure liquid coolant. Comparison example 2 A weight average molecular weight for each poly methyl meta [khu relay [thu colored resin composition including the number 2 and number [...] point high pressure liquid coolant, the artificial marble number the same method in the embodiment 1 was high pressure liquid coolant. Experiment example 1 Said in the embodiment 1, 2 and comparison example 1, 2 the number prepared by the artificial marble by picture, shown also to 1. In Figure 1, in number in the embodiment 1 (is) is prepared by the artificial marble, (or) in number in the embodiment 2 is prepared by the artificial marble, in comparison example number 1 (disclosed) is prepared by the artificial marble, in comparison example 2 and the part of the surface of the artificial marble prepared by the number (as) is disclosed. As in Figure 1 the, number 2 acrylic-based resin having a weight average molecular weight-average molecular weight of comparison example 1 white marble has same number 1 acrylic resin of draft free [...] address not apparent in patterns. Weight average molecular weight of less than number 1 number 2 acrylic resin of example 2 compared to the weight average molecular weight of acrylic resin in the case of the east that [lah of the sprocket and a draft free of artificial marble white [...] bicycle extends long in the tropics. While, acrylic-based resin having a weight average molecular weight average molecular weight of higher than number 1 number 2 in the embodiment 1 of draft free of white marble has an acrylic resin extends long in the [...] filters amorphous collective line light from beauty to the pattern and an indirectly-form can be obtained. In addition, the motion direction swizzle stick ultraviolet elongated of wood on high molecular weight has been confirmed. In addition, acrylic-based resin having a weight average molecular weight average molecular weight of acrylic resin number 1 number 2 in the embodiment 2 much higher than the elongate thin throughout the artificial marble of marble has clear amorphous beauty and an indirectly-rubber can be provided. Of the present invention preferred embodiment of the present invention detailed above for the SFC but not limited to rights range and then basic general outline of the present invention defined in the claims of which using one skilled in addition of the present invention in a range of various modified and improved form rights are disclosed. Provided is an artificial marvel composition comprising a base resin composition and a colored resin composition. The base resin composition comprises a first acrylic resin, a first acrylic monomer and a first inorganic filler. The colored resin composition comprises a second acrylic resin, a second acrylic monomer, a second inorganic filler and an inorganic pigment. The weight-average molecular weight (Mw) of the first acrylic resin is higher than the Mw of the first acrylic resin. Artificial marble, which is a cured product of the artificial marvel composition, can implement a marble pattern close to natural marble. COPYRIGHT KIPO 2017 Base resin composition; and colored resin composition; and, said base resin composition number 1 acrylic resin, number number 1 and number 1 acryl-based monomer and an inorganic filler, said colored resin composition number 2 acrylic resin, acryl-based monomer number 2, number 2 and number and draft free [...] inorganic filler, said number 2 acrylic resin weight-average molecular weight (Mw) weight-average molecular weight (Mw) high artificial representation three than is said number 1 acrylic resin composition. According to Claim 1, weight-average molecular weight (Mw) is 6 to 10 only said number 1 acrylic resin for each artificial marble composition. According to Claim 1, said number 2 is only 12 to 40 weight average molecular weight of acrylic resin (Mw) for each artificial marble composition. According to Claim 1, said base resin composition to said colored resin composition including artificial marble composition 7:3 to 9:1 weight ratio. According to Claim 1, said colored resin composition in said base resin composition viscosity and viscosity 25 °C 60Ps is and to 100Ps trillion representation three composition. According to Claim 5, said colored resin composition viscosity of said base resin composition viscosity difference is and 20 Ps hereinafter trillion representation three composition. According to Claim 1, 100 parts by weight of said base resin composition number 1 acrylic resin, number 1 to 70 parts by weight of an inorganic filler number 150 to 400 parts by weight of acryl-based monomer number 1 275 including artificial marble composition. According to Claim 1, said colored resin composition number 2 acrylic resin 100 parts by weight, to 100 parts by weight of 1,800 acryl-based monomer number 2, number 2 number 90 parts by weight of an inorganic filler material to 1,100 draft free 0. 1 To 8 parts by weight of a composition including artificial marble. According to Claim 1, said number 1 acrylic resin and said number 2 acrylic resin, independently, (meta) methyl methacrylate, ethyl (meta) methacrylate, butyl (meth) methacrylate, 2 - ethylhexyl (meth) methacrylate, benzyl methacrylate (meta), a dimethylaminoethyl methacrylate and combinations thereof selected from the group consisting of glycidyl (meta) polymer or copolymer or glass fiber composition. According to Claim 1, said number 1 acryl-based monomer and said number 2 acrylic monomers are, independently, (meta) methyl methacrylate, ethyl (meta) methacrylate, butyl (meth) methacrylate, 2 - ethylhexyl (meth) methacrylate, benzyl methacrylate (meta), glycidyl (meta) dimethylaminoethyl methacrylate and combinations thereof selected from the group consisting one including artificial marble composition. According to Claim 1, said number 1 number and said number 2 number inorganic filler is an inorganic filler, independently, aluminum hydroxide, magnesium hydroxide, calcium carbonate, silica, alumina and combinations thereof selected from the group consisting one including artificial marble composition. According to Claim 1, said number 1 number m to 100 m is and said number 2 number mean particle size of the inorganic filler and an inorganic filler 25 micro micro trillion representation three composition. According to Claim 1, said artificial marble composition inorganic chip, crosslinked number, polymerization disclosure number and combination thereof further including one selected from the group consisting number addition of artificial marble composition. According to Claim 1, further including said base resin composition inorganic chip artificial marble composition. Number 1 to number 14 of the composition for an artificial marble either anti anti according to artificial marble. Number 1 acrylic resin, an inorganic filler and a resin composition including the step number 1 number 1 acryl-based monomer and base number tank number; number 2 acrylic resin, acryl-based monomer number 2, number 2 and number draft free colored resin composition including an inorganic filler [...] step number tank; said base resin composition and said colored resin composition by mixing artificial marble composition step number bath; the beauty of wood on said artificial marble composition of a sample (agitator) step; and said beauty are coated directly on the artificial marble composition for thermosetting step; and, said number 2 acrylic resin weight-average molecular weight (Mw) said number 1 acrylic resin weight-average molecular weight (Mw) is higher artificial marble manufacturing method. According to Claim 16, said inorganic chip manufacturing method further including artificial marble base resin composition. According to Claim 16, based on the weight of said base resin composition to said colored resin composition 7:3 to 9:1 artificial marble manufacturing method.
