Steel sheet having hot-dip galvanized layer and exhibiting superior plating wettability and plating adhesion, and production method therefor

Provided are a steel sheet that has a hot-dip galvanized layer and that exhibits superior plating wettability and plating adhesion, and a production method therefor. A steel sheet containing readily oxidizable elements including Si and Mn is used as a base material. The hot-dip galvanized steel sheet has a hot-dip galvanized layer (A) on the surface of the steel sheet and is characterized by having a (B) layer that is directly under the surface of and inside of the steel sheet. The (B) layer has a thickness of 0.001 mum to 0.5 mum. By mass, the (B) layer contains 50 mass% or more of unoxidized Fe, less than 50 mass% total of one or more oxides of Fe, Si, Mn, P, S, and/or Al, and contains unoxidized C, Si, Mn, P, S, and/or Al in the following quantities: less than 0.05 mass% of C; less than 0.1 mass% of Si; less than 0.5 mass% of Mn; less than 0.001 mass% of P; less than 0.001 mass% of S; and less than 0.005 mass% of Al.