BONDING METHOD, METHOD FOR MANUFACTURING STRUCTURE, AND STRUCTURE
This application is a Continuation of PCT International application Ser. No. PCT/JP2015/056140 filed in Japan on Mar. 3, 2015, which claims the benefit of Patent Application No. 2014-136226 filed in Japan on Jul. 1, 2014, the entire contents of which are hereby incorporated by reference. The present invention relates to a method for bonding two members to each other by use of an adhesive. The present invention also relates to a structure including two members which are bonded to each other and a method for manufacturing the structure. As a method for bonding two members to each other, a bonding method using solder and a bonding method using an adhesive have widely been used. For example, solder is used for bonding an electronic component to a submount of a laser module and an adhesive is used for bonding an optical component to the submount of the laser module. In a case where the electronic component and the optical component are bonded to the submount, the following problem occurs. That is, in a case where the electronic component is bonded to the submount by use of solder, it is necessary to plate a surface of the submount with gold in order to obtain sufficient bonding strength. However, a gold-plated surface of the submount makes it difficult to bond the optical component to the submount by use of an adhesive. The following describes why it is difficult to bond a member to another member having a surface plated with gold. That is, bonding by an adhesive is typically strengthened by intermolecular force generated between molecules constituting the adhesive and atoms or molecules constituting a surface to be bonded of a member. However, since gold atoms are nonpolar atoms, in a case where the surface to be bonded is made of gold, it is impossible to strengthen the bonding by the adhesive by using the intermolecular force. Patent Literature 1 discloses a bonding method as a technique usable for avoiding the problem. According to the bonding method disclosed in Patent Literature 1, an FIPG (Formed In Place Gasket) which has high bonding strength with respect to metal is used for bonding a metal member and a synthetic resin member to each other. [Patent Literature 1] Japanese Patent Application Publication, Tokukai, No. 2013-199834 (Publication date: Oct. 3, 2013) However, a technique of bonding a second member (e.g., optical component) to a first member (e.g., submount) having a gold-plated surface requires, in addition to use of the FIPG as an adhesive, a step of providing, on a surface of the second member, a synthetic resin material containing aluminum powder. Further, use of the technique also requires a step of causing a synthetic resin material to contain aluminum powder and a step of appropriately controlling the synthetic resin material. For this reason, there is a demand for realization of a bonding method which is a method for bonding a gold-plated first member and a second member to each other and is capable of achieving a high adhesive force without carrying out any special treatment on the second member. The present invention has been accomplished in view of the problem, and an object of the present invention is to provide a bonding method which is a method for bonding a first member and a second member to each other and is capable of achieving a high adhesive force without carrying out any special treatment on the second member, even in a case where the first member has a surface on which a gold thin film is formed. Another object of the present invention is to provide a manufacturing method and a structure each of which brings about an effect similar to that of the bonding method. In order to attain the object, a bonding method in accordance with the present invention is a bonding method for bonding a first member and a second member to each other, the first member being made of a material other than gold and having a surface on which a gold thin film is formed, the second member being made of a material other than gold, the bonding method including the steps of: (1) irradiating, with laser light, at least part of a specific region of the surface of the first member, so that a base of the thin film is exposed in the at least pan of the specific region; and (2) bonding the second member to the specific region by use of an adhesive. In order to attain the object, a manufacturing method for manufacturing a structure including a first member and a second member, the first member being made of a material other than gold and having a surface on which a gold thin film is formed, the manufacturing method including the steps of: (1) irradiating, with laser light, a specific region of the surface of the first member, so that a base of the thin film is exposed in the specific region; and (2) bonding the second member to the specific region by use of an adhesive. In order to attain the object, a structure in accordance with the present invention is a structure including: a first member; and a second member, the first member being made of a material other than gold and having a surface on which a gold thin film is formed, the surface of the first member containing a specific region in which a base of the thin film is exposed by irradiation with laser light, the second member being bonded to the specific region by use of an adhesive. With the present invention, it is possible to achieve a high adhesive force without carrying out any special treatment on the second member, even in a case where the first member has a surface on which a gold thin film is formed. (a) of (a) and (b) of (a) and (b) of The following description will discuss, with reference to (a) of The bonding method S1 is a method for bonding a first member 11 and a second member 14 to each other and includes an irradiation step S11 and a bonding step S12 as illustrated in (a) of (b) of Embodiment 1 employs, as the first member 11, a member in which, on a surface of a copper base material 11 The irradiation step S11 is a step of irradiating, with laser light, at least part of a specific region (hereinafter referred to as “irradiation region”) 12 In Embodiment 1, each point in the irradiation region 12 The bonding step S12 is a step of bonding the second member 14 to a specific region (hereinafter referred to as “bonding region”) 12 In Embodiment 1, a photocurable resin such as an ultraviolet curable resin is employed as a material of the adhesive 13 and a transparent material such as glass is employed as a material of the second member 14. This makes it possible to irradiate the adhesive 13 with light (e.g., ultraviolet) through the second member 14, so that the bonding step S12 can be easily carried out. Note, however, that the material of the second member 14 is not limited to the transparent material, but can be selected from any materials other than gold. Further, the adhesive 13 is not limited to the photocurable resin which is cured by light, but can be a resin which is cured by heat or a chemical reaction. In Embodiment 1, as illustrated in (c) of As described above, according to the bonding method S1 in accordance with Embodiment 1, (1) the base of the thin film 12 is exposed in the at least part of the irradiation region 12 Note that the bonding method S1 in accordance with Embodiment 1 is also applicable to a method for manufacturing the structure 1. An optical module can be an example of the structure 1 which can be manufactured by the bonding method S1 in accordance with Embodiment 1. In the optical module, (1) a laser light source (e.g., a laser diode (LD)) which emits laser light, (2) an electronic component for driving the LD, (3) an optical member (e.g., a mirror or a lens) which directs the laser light to an optical fiber, and the like are provided on a substrate or a submount stacked on the substrate. Note that a surface of the substrate or the submount is often plated with gold. Thus, the bonding method in accordance with the present invention is applied when the substrate or the submount (corresponding to the first member 11) and the optical member (corresponding to the second member 14) are bonded to each other. This makes it possible to favorably bond the optical member to the surface of the substrate or the submount by use of an adhesive, even in a case where the surface of the substrate or the submount is plated with gold. The structure 1 (e.g., the optical module) which is manufactured by the bonding method S1 in accordance with Embodiment 1 is also encompassed in the scope of the present invention. The following description will discuss examples of the bonding method S1 with reference to Note that Examples 1 through 4 employed, as the first member 11, a member in which on a surface of a copper base material 11 In the irradiation step S11, each of irradiation points which were distributed at a predetermined density in an irradiation region 12 In the bonding step S12, (1) an adhesive 13 (ultraviolet curable resin) was applied to the bonding region 12 As shown in Note that the ratio of the Au-plated region was obtained by (i) extracting, by carrying out image processing, a region in which the thin film 12 remained in a photograph obtained by capturing an image of the irradiation region 12 As shown in In a case where an optical module is manufactured by the bonding method S1, the bonding stress between the first member 11 and the second member 14 is preferably not less than 1.4 MPa. This is based on the finding that, in the optical module, a substrate or a submount which corresponds to the first member 11 may be warped by 10 μm at the maximum. The inventors of the present application found that in a case where the substrate or the submount is warped by 10 μm, a bending stress of approximately 1.4 MPa at the maximum is generated in a bonding region 12 According to the results of measurement of bonding stress shown in As described above, in the bonding method S1, the bonding stress between the first member 11 and the second member 14 increases as the number of times the irradiation step S11 is carried out increases. This is primarily because as the number of times at which the irradiation step S11 is carried out increases, the ratio of the Au-plated region in the irradiation region 12 The following description will discuss, with reference to (a) and (b) of The modified example illustrated in (a) of The modified example illustrated in (b) of With the configuration, since the second member 14 is bonded to the irradiation region 12 The following description will discuss, with reference to The modified example illustrated in (a) of Note, however, that in a case where a region of the irradiation region 22 The modified example illustrated in (b) of With the configuration, since the irradiation region 22 In Modified Example 2, (b) of [Conclusion] A bonding method in accordance with Embodiment 1 is a bonding method for bonding a first member and a second member to each other, the first member being made of a material other than gold and having a surface on which a gold thin film is formed, the second member being made of a material other than gold, the bonding method including the steps of: (1) irradiating, with laser light, at least part of a specific region of the surface of the first member, so that a base of the thin film is exposed in the at least part of the specific region; and (2) bonding the second member to the specific region by use of an adhesive. With the configuration, the second member is bonded to the base which is made of the material other than gold, instead of being bonded to the gold thin film. This makes it possible to achieve a higher adhesive force without carrying out any special treatment on the second member, as compared with a case where the second member is bonded to the gold thin film. The bonding method in accordance with Embodiment 1 is preferably configured such that the step (1) is a step of sporadically irradiating each point in the specific region with laser light. With the configuration, regions in each of which the base is exposed can be densely scattered in the irradiation region. Further, in a case where the step (1) is repeatedly carried out, it is possible to (i) gradually increase, in the specific region, a ratio of the regions in each of which the base is exposed and (ii) gradually reduce, in the specific region, a ratio of a region in which the thin film remains. The bonding method in accordance with Embodiment 1 is preferably configured such that the step (1) is repeated until a sum total of an area of a region in which the thin film remains in the specific region becomes not more than 60% of an area of the specific region. With the configuration, a bonding stress between the first member and the second member exceeds a predetermined value (1.4 MPa) which is considered to be sufficient for practical use. The bonding method in accordance with Embodiment 1 is preferably configured such that the specific region is contained in a region to which the second member is bonded on the surface of the first member. The configuration makes it possible to prevent the base of the thin film from coming into contact with outside air after the step (2) is carried out. Accordingly, it is possible to prevent a deterioration such as corrosion of the base of the thin film. The bonding method in accordance with Embodiment 1 is preferably configured such that the specific region is a region whose outer circumference is constituted by a smooth curved line. With the configuration, the outer circumference of the specific region has no angular corner on which a bending stress is likely to concentrate. Accordingly, a bending stress which is generated when the first member is warped is dispersed on the outer circumference of the specific region. This makes it possible to more strongly bond the first member and the second member to each other, as compared with a case where the outer circumference of the specific region has an angular corner. The bonding method in accordance with Embodiment 1 is preferably configured such that the specific region is an annular region which extends along an outer circumference of a region to which the second member is bonded on the surface of the first member. The configuration allows an area of the irradiation region to be smaller. This makes it possible to reduce a time required for the step (1). The bonding method in accordance with Embodiment 1 is preferably configured such that the second member is a transparent member. The configuration makes it possible to irradiate the adhesive with light (e.g., ultraviolet) through the second member, so that the step (2) can be easily carried out. A manufacturing method in accordance with Embodiment 1 is a manufacturing method for manufacturing a structure including a first member and a second member, the first member being made of a material other than gold and having a surface on which a gold thin film is formed, the manufacturing method including the steps of: (1) irradiating, with laser light, a specific region of the surface of the first member, so that a base of the thin film is exposed in the specific region; and (2) bonding the second member to the specific region by use of an adhesive. The manufacturing method in accordance with Embodiment 1 brings about an effect similar to that of the bonding method in accordance with Embodiment 1. A structures. in accordance with Embodiment 1 is a structure including: a first member; and a second member, the first member being made of a material other than gold and having a surface on which a gold thin film is formed, the surface of the first member containing a specific region in which a base of the thin film is exposed by irradiation with laser light, the second member being bonded to the specific region by use of an adhesive. The structure in accordance with Embodiment 1 brings about an effect similar to that of the bonding method in accordance with Embodiment 1. [Additional Remarks] The present invention is not limited to the embodiments, but can be altered by a skilled person in the art within the scope of the claims. An embodiment derived from a proper combination of technical means each disclosed in a different embodiment is also encompassed in the technical scope of the present invention. The present invention is applicable to a bonding method for bonding two members to each other by use of an adhesive. Further, the present invention is applicable to a structure including two members which are bonded to each other and a manufacturing method for manufacturing the structure. S1: Bonding method S11: Irradiation step S12: Bonding step 1: Structure 11: First member 11 11 11 12: Thin film 12 12 13: Adhesive 14: Second member The present invention provides a bonding method (S1) which is capable of achieving a high adhesive force without carrying out any special treatment on the second member (14), even in a case where the first member (11) has a surface on which a gold thin film (12) is formed. The first member (11) is made of a material other than gold and has a surface on which the gold thin film (12) is formed. The bonding method (S1) includes the steps of: (S11) irradiating, with laser light, at least part of a specific region (12a) of the surface of the first member (11), so that a base of the thin film (12) is exposed in the at least part of the specific region (12a); and (S12) bonding the second member (14) to the specific region (12a) by use of an adhesive (13). 1. A bonding method for bonding a first member and a second member to each other, the first member being made of a material other than gold and having a surface on which a gold thin film is formed, the second member being made of a material other than gold,
said bonding method comprising the steps of: (1) irradiating, with laser light, at least part of a specific region of the surface of the first member, so that a base of the thin film is exposed in the at least part of the specific region; and (2) bonding the second member to the specific region by use of an adhesive. 2. The bonding method as set forth in 3. The bonding method as set forth in 4. The bonding method as set forth in 5. The bonding method as set forth in 6. The bonding method as set forth in 7. The bonding method as set forth in 8. A manufacturing method for manufacturing a structure including a first member and a second member, the first member being made of a material other than gold and having a surface on which a gold thin film is formed,
said manufacturing method comprising the steps of: (1) irradiating, with laser light, a specific region of the surface of the first member, so that a base of the thin film is exposed in the specific region; and (2) bonding the second member to the specific region by use of an adhesive. 9. A structure comprising:
a first member; and a second member, the first member being made of a material other than gold and having a surface on which a gold thin film is formed, the second member being made of a material other than gold, the surface of the first member containing a specific region in at least part of which a base of the thin film is exposed by irradiation with laser light, the second member being bonded to the specific region by use of an adhesive.CROSS-REFERENCE TO RELATED APPLICATIONS
TECHNICAL FIELD
BACKGROUND ART
CITATION LIST
Patent Literature
SUMMARY OF INVENTION
Technical Problem
Solution to Problem
Advantageous Effects of Invention
BRIEF DESCRIPTION OF DRAWINGS
DESCRIPTION OF EMBODIMENTS
EXAMPLES
Modified Example 1
Modified Example 2
INDUSTRIAL APPLICABILITY
REFERENCE SIGNS LIST